High Fatigue Resistance 1-4mm Thickness Twill Weave Carbon Fiber Sheets and Plates

High Fatigue Resistance 1-4mm Thickness Twill Weave Carbon Fiber Sheets and Plates

Carbon fiber sheets and plates are flat, rigid materials made from layers of carbon fiber-reinforced polymer (CFRP). They are known for their lightweight, high strength, and durability, making them ideal for a wide range of applications, including aerospace, automotive, sporting goods, and construction.

Application

• Aerospace: Used in manufacturing fuselage components, wing surfaces, and interior parts to enhance aircraft performance and fuel efficiency.
• Automotive Industry: Used in making body panels, chassis parts, and interior structures to reduce vehicle weight and improve fuel economy.
• Consumer Electronics: Utilized in producing laptop shells, smartphone back covers, and other components, offering lightweight and durable solutions.
• Medical Equipment: Applied in the production of lightweight medical devices, such as operating tables and wheelchairs, to improve ease of use.
• Sports Equipment: Used in the manufacture of bicycle frames, tennis rackets, and other sports gear, providing high-strength, lightweight equipment.
• Building Materials: Employed in constructing building components like curtain walls and staircases, enhancing the durability and aesthetics of structures.

Carbon Fiber Flat Plate Specification:

Production Process of Carbon Fiber Sheets and Plates

1. Raw Material Preparation: Prepreg Preparation: Use high-quality prepreg (carbon fiber fabric impregnated with epoxy resin) to ensure uniform resin content and carbon fiber alignment.

2. Cutting the Prepreg: Cutting: Cut the prepreg to the required size and shape according to the design specifications. Ensure clean edges during cutting to maintain accuracy in the subsequent lamination process.

3. Lamination: Laminating: Stack the cut prepreg layers according to the desired thickness and strength. Each layer of prepreg should be arranged in a specific direction to achieve optimal mechanical properties.

4. Placing in the Mold: Mold Preparation: Select an appropriate mold and place the stacked prepreg into the mold, ensuring the prepreg is flat and wrinkle-free. The mold surface should be treated with a release agent to facilitate demolding.

5. Vacuum Bagging: Bagging: Use a vacuum bag to seal the mold and prepreg, ensuring a good seal. The purpose of vacuum bagging is to remove air and prevent the formation of bubbles and voids during the autoclave process.

6. Autoclave Curing

• Curing: Place the sealed mold into the autoclave, setting the appropriate temperature, pressure, and time for curing. The typical curing temperature ranges from 120-180°C, with a pressure of 5-7 bar. The specific parameters are adjusted according to the properties of the prepreg and product requirements.
• Solidification: During the autoclave process, the resin in the prepreg will flow and cure, forming a solid and robust carbon fiber board structure.

7. Demolding

• Cooling: After curing, allow the mold and carbon fiber board to cool naturally to room temperature.
• Demolding: Carefully remove the carbon fiber board from the mold, ensuring no damage to the surface.

8. Post-Processing

• Trimming: Use cutting equipment to trim the edges of the carbon fiber board to achieve the final dimensions and shape.
• Surface Treatment: Perform surface treatments (such as sanding or coating) to achieve a smooth or matte finish as per customer requirements.

4mm Thickness Carbon Fiber Sheets

High Fatigue Resistance Carbon Fiber Sheets

Twill Weave Carbon Fiber Sheets

High Fatigue Resistance 1-4mm Thickness Twill Weave Carbon Fiber Sheets and Plates Images